Lithopone

Industrial Grade Inorganic Pigment Lithopone CAS 345-05-7

상품명:
Lithopone
등급:
Industrial Grade
속성:
백색 분말
포장:
25kg/드럼
MOQ:
1 kilo
저장:서늘하고 건조한 장소
유효기간:2 년

지금 연락하세요 PDF 다운로드

세부

태그

제품 설명

A mixture of zinc sulfide and barium sulfate, also known as zinc barium white, white crystalline powder. It is a mixture of zinc sulfide and barium sulfate. The more zinc sulfide it contains, the stronger its covering power and the higher its quality.

<trp-post-container data-trp-post-id='10990'>Lithopone</trp-post-container>

애플리케이션

1 .Ink is a kind of viscous fluid composed of color material, filler, additive and color developing agent. At present, printing newspapers, books, pictures and printing iron, printing metal, printing porcelain, printing rubber, printing plastic and printing radio semiconductor circuit boards are inseparable from ink. Because titanium dioxide has a large hiding power, high achromatous power, fine particles, dilute acid dilute alkali resistance, light resistance, heat resistance, not easy to yellowing, good hydrophobicity, small fluidity, insoluble in the color development agent and can be evenly dispersed in the color development agent, it is an indispensable color of advanced white ink and light ink.

2 Paint is a viscous suspension composed of pigments, oils, paints (resins), solvents and drying agents. White pigment is the most widely used pigment, white paint and light paint are used in it, so in the paint, the amount of white pigment is much more than other pigments. The white pigments that can be used to make paint are often zinc white, zinc barium white and titanium dioxide. Due to the development of coating industry varieties, the emergence of synthetic resin coatings, its polymerization degree is large, such as adding zinc white, because of the zinc white alkaline, and the free fatty acid in the coating, and have a tendency to thicken; If zinc barium white is added, the weather resistance is poor. However, the use of titanium dioxide can improve the above shortcomings, because the particles of titanium dioxide are small and uniform, the photochemical stability is high, the covering rate is more than two times that of zinc white, zinc barium white, and the achromatic power is 5 to 6 times, so the amount of pigment in the entire paint can be greatly reduced. At the same time, the paint made is good in color, not easy to yellow, and has chemical stability such as heat resistance and acid resistance, sulfur resistance, alkali resistance, especially rutile titanium dioxide, its structure is stable, weather resistance is better than anatase type, ultraviolet radiation resistance, outdoor will not powder and other advantages. Therefore, it is suitable for all kinds of high-grade ships, Bridges, automobiles, buildings and other outdoor coatings with high weather resistance. Anatase titanium dioxide is generally only used for indoor paint. It can be seen that titanium dioxide has become an essential white pigment in the production of coatings. About 60% of the world's titanium dioxide is used in the production of various coatings.

장점

우리는 고품질의 제품과 경쟁력 있는 가격을 제공할 수 있는 깊은 협력을 바탕으로 많은 고품질 공장을 보유하고 있습니다. 또한 대량 구매 시 할인 혜택도 제공할 수 있습니다. 또한 많은 전문 화물 운송 회사와 협력하여 안전하고 원활하게 제품을 귀하의 손에 전달할 수 있습니다. 배송기간은 결제 확인 후 약 3~20일 정도 소요됩니다.

사양

Parameters	B311	B301
Total zinc and Barium sulphate, %	≥99.0	≥99.0
zinc sulfide content, %	≥30.0	≥28.0
zinc oxide content, %	≤0.3	≤0.6
Color, compared with standard samples	better	better
Tinter reducing power	≥105	≥100
105°C volatile matter, %	≤0.3	≤0.3
Water solubles, %	≤0.3	≤0.4
Water suspension pH-value	6.0-8.0	6.0-8.0
Oil absorption, g/ 100g	≤14	≤14
Hiding power	≥ 5 % of standard sample	≥ 5 % of standardsample