The COSIL F series of hydroxypolysiloxanes is a hydroxyl terminated polydimethylsiloxane. It is a series of functional polymers with different viscosities and different contents of terminal hydroxyl groups. Low-viscosity polymers can be used for filler surface treatment and anti-structuring additives for high-temperature adhesives, and can also be used in room-temperature adhesive formulations. Low-viscosity hydroxy silicone oils can also be used as reactive diluents to adjust the overall viscosity of the formulation.

Hydroxy silicone oil is made by polymerization of siloxane monomers, the molecular silicone materials have hydroxyl groups at both ends. The structural formula is as follows:

HO-Si (CH3) 2 O [Si (CH3) 2 O] n Si(CH3)2-OH

Chemical name is a, w- dihydroxy polydimethylsiloxane
It name 107 silicone rubber when the viscosity is above 2500mPa.S.
In addition to the general performance of methyl silicone oil, it also has reactive hydroxyl groups, it can be made available some new material or crosslinked into elastomers (or membrane) .

Colorless transparent liquid with excellent electrical insulating properties and resistance to high temperature, high flash point, low freezing point, long-term used -50 o C ~ +250 o C conditions, low the viscosity-temperature coefficient, high compression ratio, low surface tension, hydrophobic moisture resistance, chemical inertness, physiologically inertness.

It is widely used in the fields of silicone rubber industry, electronic appliances, building materials, leather material processing, plastic processing, motor manufacturing, petrochemical industry, textile printing and dyeing, medicine and health and technology.

우리는 고품질의 제품과 경쟁력 있는 가격을 제공할 수 있는 깊은 협력을 바탕으로 많은 고품질 공장을 보유하고 있습니다. 또한 대량 구매 시 할인 혜택도 제공할 수 있습니다. 또한 많은 전문 화물 운송 회사와 협력하여 안전하고 원활하게 제품을 귀하의 손에 전달할 수 있습니다. 배송기간은 결제 확인 후 약 3~20일 정도 소요됩니다.

이 제품은 무엇인가요?

Usually with the curing agent to achieve the crosslinking, it must be fixed by means of a coupling agent for the release paper, generally the curing agent is about 3 to 5% of gum base, the coupling agent is about 0.5 to 1 % of gum base.

In most cases the solvent was diluted with 10 times the first gum base, then add the coupling agent and the curing agent after mixing uniformly coated on the substrate surface at room temperature or heat curing.  It need over 30 minutes at room temperature,  and 30 seconds for 120 ~ 150 o C. there is no need any solvents for sealants and molds for rubber, add the curing agent and stir ( one-component and two-component curing agent is used is not the same ) , after 30 to 120 minutes degassing it can be cured .

애플리케이션

Depending on the hydroxyl content and viscosity, respectively for different industries .

1. the medium-high viscosity of the product can be used as a paper -based of anti- adhesive agent, the cured film has excellent anti-sticking effect, such as the label backing paper , asphalt wrapping, sealing tape base paper, decor paper end paper processing.
2. in the electrical power industry as the main component insulating paint or a component of the insulator.
3. Used as a condensation-type RTV silicone rubber based adhesive and diluted material, such as sealants and plastic mold base material.
4. Alter dimethyl silicone oil, and easy to emulsify .
5. Small molecule hydroxyl silicone oil (25 ~ 30CP, hydroxyl content of about 8%) is an excellent control agent of silicone rubber, it not only simplifies the process of silicone rubber to improve the processing performance ( reduce heat treatment ) but also increased the transparency of products, improved working conditions .
6. New development applications.